X6CrNiMoNb17-12-2, 1.4580, AISI 316Cb, UNS S31640 - Manyleb a Chymhwysiad
X6CrNiMoNb17-12-2, 1.4580, AISI 316Cb, UNS S31640 - Manyleb a Chymhwysiad
- EN 10028-7 - Cynhyrchion gwastad wedi'u gwneud o ddur at ddibenion gwasgedd - Rhan 7: Dur di-staen
- EN 10088-1 - Dur di-staen - Rhan 1: Rhestr o ddur di-staen
- EN 10088-2 - Dur di-staen - Rhan 2: Amodau cyflenwi technegol ar gyfer dalen / plât a stribed o ddur sy'n gwrthsefyll cyrydiad at ddibenion cyffredinol
- EN 10088-3 - Dur di-staen - Rhan 3: Amodau cyflenwi technegol ar gyfer cynhyrchion lled-orffen, bariau, gwiail, gwifrau, adrannau a chynhyrchion llachar dur sy'n gwrthsefyll cyrydiad at ddibenion cyffredinol
- EN 10216-5 (2004) - Tiwbiau dur di-dor at ddibenion gwasgedd - Amodau cyflenwi technegol - Rhan 5: Tiwbiau dur di-staen
- EN 10272 - Bariau dur di-staen at ddibenion gwasgedd
- EN 10297-2 (2005) - Tiwbiau dur crwn di-dor at ddibenion peirianneg fecanyddol a chyffredinol - Amodau cyflenwi technegol - Rhan 2: Dur di-staen
a ddefnyddir ar gyfer caewyr, cyfnewidwyr gwres, oeryddion, tanciau, pympiau, piblinellau ac offer tebyg purfeydd, melinau papur, gweithfeydd prosesu bwyd a gweithfeydd cemegol
Cyfansoddiad cemegol(wt. y cant) o X6CrNiMoNb17-12-2, 1.4580, AISI 316Cb, gradd UNS S31640: i EN 10028-7
| Elfennau | Isafswm. （ Mwy na neu'n hafal i ） | Uchafswm. （ Llai na neu'n hafal i ） | Tebyg | Sylwadau |
|---|
| C | - | 0.080 |
|
|
| Si | - | 1.00 |
|
|
| Mn | - | 2.00 |
|
|
| P | - | 0.045 |
|
|
| S | - | 0.015 |
|
|
| Cr | 16.50 | 18.50 |
|
|
| Mo | 2.00 | 2.50 |
|
|
| Ni | 10.50 | 13.50 |
|
|
| Nb | 10×C | 1.00 |
|
|
Priodweddau mecanyddol gradd X6CrNiMoNb17-12-2, 1.4580, AISI 316Cb, gradd UNS S31640: i EN 10028-7
Cryfder Cynnyrch,Rp 0.2(MPa)
| Cyflwr | Minnau | Max | Tebyg | Nodyn |
|---|
| Forgings | 220 | 250 |
|
|
| Tymheredd uchel 50 gradd | 207 |
|
|
|
| Tymheredd uchel 150 gradd | 177 |
|
|
|
Cryfder Tynnol, Rm(MPa)
| Cyflwr | Minnau | Max | Tebyg | Nodyn |
|---|
| Forgings | 520 | 720 |
|
|
| Tymheredd uchel 50 gradd | 490 |
|
|
|
| Tymheredd uchel 150 gradd | 410 |
|
|
|
Effaith,Kv/Ku(J)
| Cyflwr | Minnau | Max | Tebyg | Nodyn |
|---|
Elongation, A ( y cant )
| Cyflwr | Minnau | Max | Tebyg | Nodyn |
|---|
| Forgings | 40 |
|
|
|
| Forgings KV. 20 gradd | 100 |
|
|
|
Lleihau arwynebedd, ( y cant )
| Cyflwr | Minnau | Max | Tebyg | Nodyn |
|---|
Caledwch
| Cyflwr | Math | Minnau | Max | Tebyg | Nodyn |
|---|
| Forgings | HBW |
| 230 |
|
|
Priodweddau ffisegol gradd X6CrNiMoNb17-12-2, 1.4580, AISI 316Cb, UNS S31640 EN 10028-7
| Dwysedd | Nodyn |
|---|
| 8 g/cm3 | Tymheredd ystafell |
| Cynhwysedd gwres penodol | Nodyn |
|---|
| 0.5 kJ/(kg*K) | Tymheredd ystafell |
| Dargludedd thermol | Nodyn |
|---|
| 15 W/(m*K) | Tymheredd ystafell |
| Modwlws Young E | Nodyn |
|---|
| 200 GPa | Tymheredd ystafell |
| Gwrthedd trydanol | Nodyn |
|---|
| 0.75 µΩ*m | Tymheredd ystafell |
| Cyfernod ehangu llinellol | Nodyn |
|---|
| 16.5 (10-6/K) | Tymheredd ystafell |
| Cyfernod ehangu llinellol | Nodyn |
|---|
| 16.5 (10-6/K) | tymheredd: 100 gradd |
Priodweddau cysylltiedig
| Triniaeth gwres a gweithio - Gofannu 1150 gradd - 850 gradd |
| Triniaeth gwres a gweithio - Rholio 1150 gradd - 850 gradd |
Triniaeth gwres a gweithio - Datrysiad 1030 gradd - 1110 gradd
|
X6CrNiMoNb17-12-2, 1.4580, AISI 316Cb, UNS S31640 - Manylion
Tiwbiau dur crwn di-dor at ddibenion peirianneg fecanyddol a chyffredinol - Amodau cyflenwi technegol - Rhan 2: Dur di-staen
X6CrNiMoNb17-12-2, 1.4580, AISI 316Cb, UNS S31640 a ddefnyddir ar gyfer caewyr, cyfnewidwyr gwres, oeryddion, tanciau, pympiau, piblinellau ac offer tebyg purfeydd, melinau papur, gweithfeydd prosesu bwyd a gweithfeydd cemegol