X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 - Manyleb a Chymhwysiad

X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 - Manyleb a Chymhwysiad

• SAE AMS 5342E (2006) - Dur, Cyrydiad-Gwrthiannol, Castings Buddsoddi 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Ateb, a Dyddodiad Trin â Gwres (H1100 ) 130 ksi (896 MPa) Cryfder Tynnol (17-4)
• SAE AMS 5343E (2006) - Dur, Cyrydiad-Gwrthiannol, Castings Buddsoddi 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Ateb, a Dyddodiad Trin â Gwres (H1000 ) 150 ksi (1034 MPa) Cryfder Tynnol (17-4)
• SAE AMS 5344F (2007) - Dur, Cyrydiad-Gwrthiannol, Castings Buddsoddi 16Cr - 4.1Ni - 0.28Cb - 3.2Cu Homogenization, Ateb, a Gwresogi Dyodiad Trin (H900) 180 ksi (1241 MPa) Cryfder Tynnol (17-4)
• SAE AMS 5604G (2013) - Dur, Gwrthsefyll Cyrydiad, Llen, Stribed, a Phlât 16.5Cr - 4.0Ni - 4.0Cu {{9} }.30Cb Ateb Wedi'i Drinio â Gwres, Dyodiad Caledadwy
• SAE AMS 5622F (2013) - Dur, Gwrth-cyrydiad, Bariau, Gwifren, Gofaniadau, Tiwbiau, a Modrwyau 16Cr - 4.0Ni - 0.30Cb{ {9}}.0Cu Datrysiad Wedi'i Drin yn Wres, Electrod Trauladwy Dyodiad Caled wedi'i Aildoddi
• SAE AMS 5643/H1150 (2013) - Dur, Gwrthsefyll Cyrydiad, Bariau, Gwifren, Gofaniadau, Tiwbiau a Modrwyau 16Cr – 4.0Ni – 0.30Cb (N. ) – 4.0Cu Datrysiad a Dyodiad Wedi'i Drin â Gwres (H1150)
• SAE AMS 5643S (2013) - Dur, Gwrthsefyll Cyrydiad, Bariau, Gwifren, Gofaniadau, Tiwbiau, a Modrwyau 16Cr - 4.0Ni - 0.30Cb{ {9}}.0Cu Datrysiad Wedi'i Drinio â Gwres, Dyodiad Caledadwy
• EN 10088-2 - Dur di-staen. Amodau cyflenwi technegol ar gyfer dalen / plât a stribed o ddur sy'n gwrthsefyll cyrydiad at ddibenion cyffredinol

Dur, Cyrydiad-Gwrthiannol, Castings Buddsoddi 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Ateb, a Gwres Dyodiad Wedi'i Drin (H1100) 130 ksi (896 MPa) Cryfder Tynnol (17-4)

Cyfansoddiad cemegol(wt. y cant) o X5CrNiCuNb17-4-4, 1.4548, AISI 630, gradd UNS S17400: i SAE AMS 5342E (2006)

Priodweddau mecanyddol gradd X5CrNiCuNb17-4-4, 1.4548, AISI 630, gradd UNS S17400: i SAE AMS 5342E (2006)

Cryfder Cynnyrch,Rp 0.2(MPa)

Cryfder Tynnol, Rm(MPa)

Effaith,Kv/Ku(J)

Elongation, A ( y cant )

Lleihau arwynebedd, ( y cant )

Caledwch

Priodweddau ffisegol gradd X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 SAE AMS 5342E (2006)

Priodweddau cysylltiedig

X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 - Manylion

SAE AMS 5342E (2006) Steel, Corydiad-Gwrthiannol, Castings Buddsoddi 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Ateb, a Dyddodiad Trin â Gwres (H1100) 130 ksi (896 MPa) Cryfder Tynnol Dur di-staen wedi'i galedu gan wlybaniaeth X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 Defnyddir yn nodweddiadol ar gyfer rhannau sydd angen ymwrthedd cyrydiad da a chryfder hyd at 315 ° C.

Cais

Dur di-staen wedi'i galedu gan wlybaniaeth X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 yw un o'r duroedd aloi cromiwm-nicel di-staen mwyaf poblogaidd a ddefnyddir amlaf gydag ychwanegyn copr, dyddodiad wedi'i galedu â strwythur martensitig. Fe'i nodweddir gan ymwrthedd cyrydiad uchel tra'n cynnal eiddo cryfder uchel, gan gynnwys caledwch. Gall dur weithredu yn yr ystod tymheredd o -29 gradd i 343 gradd, tra'n cadw paramedrau cymharol dda. Yn ogystal, nodweddir y deunyddiau yn y radd hon gan hydwythedd cymharol dda ac mae eu gwrthiant cyrydiad yn debyg i ddur caledu dyddodiad di-staen X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400